LSR For Miscellaneous Pieces (Coating)

LSR For Miscellaneous Pieces (Coating)
Request a Quote
Applications

This liquid silicone rubber (LSR) can be used as coating materials for electrical and electronic components, sponge sheets and fiberglass cloth.

Features
  • Rapid vulcanization, good dimensional stability and processability;
  • Non-toxic and safe, food grade;
  • High tear strength, non-yellowing;
Approvals

ROHS, REACH, FDA, CA65, EN71-3, EN14372, PAHS, PFOA, CPSIA, Dimethyl Cyclosiloxane, etc.

Test

Rheometer test, 120℃, 5min

Technical Data
  • Model: HT-T7200A/B
  • Appearance: Translucent
  • Viscosity: 2W-3W
  • Hardness (Shore A): 20
  • Density (g/cm3): 1.06
  • Tensile strength (Mpa): 6
  • Elongation (%): 700
  • Tear strength (K N/m): 15
  • Model: HT-T7300A/B
  • Appearance: Translucent
  • Viscosity: 2W-3W
  • Hardness (Shore A): 30
  • Density (g/cm3): 1.08
  • Tensile strength (Mpa): 6
  • Elongation (%): 700
  • Tear strength (K N/m): 15
  • Model: HT-T7400A/B
  • Appearance: Translucent
  • Viscosity: 2W-3W
  • Hardness (Shore A): 40
  • Density (g/cm3): 1.1
  • Tensile strength (Mpa): 7
  • Elongation (%): 650
  • Tear strength (K N/m): 20
  • Model: HT-T7500A/B
  • Appearance: Translucent
  • Viscosity: 2W-3W
  • Hardness (Shore A): 50
  • Density (g/cm3): 1.12
  • Tensile strength (Mpa): 7
  • Elongation (%): 600
  • Tear strength (K N/m): 25
  • Model: HT-T7600A/B
  • Appearance: Translucent
  • Viscosity: 2W-3W
  • Hardness (Shore A): 60
  • Density (g/cm3): 1.12
  • Tensile strength (Mpa): 7
  • Elongation (%): 450
  • Tear strength (K N/m): 25
  • Model: HT-T7700A/B
  • Appearance: Translucent
  • Viscosity: 2W-3W
  • Hardness (Shore A): 70
  • Density (g/cm3): 1.14
  • Tensile strength (Mpa): 8
  • Elongation (%): 400
  • Tear strength (K N/m): 20
  • Model: HT-T7800A/B
  • Appearance: Translucent
  • Viscosity: 2W-3W
  • Hardness (Shore A): 80
  • Density (g/cm3): 1.14
  • Tensile strength (Mpa): 7
  • Elongation (%): 260
  • Tear strength (K N/m): 15